Effect of Temperature Variation on Wear Behaviour of Austenitic Stainless Steel

• Published in: IOP Conference Series: Materials Science and Engineering
• Main Author: 2-s2.0-85012271921
• Format: Conference paper
• Language: English
• Published: Institute of Physics Publishing 2016
• Online Access: https://www.scopus.com/inward/record.uri?eid=2-s2.0-85012271921&doi=10.1088%2f1757-899X%2f160%2f1%2f012026&partnerID=40&md5=5a35bf3b8c220799b996e8db313f95f6
• ISSN: 17578981
• DOI: 10.1088/1757-899X/160/1/012026

The effects of boronizing temperatures on the wear and hardness properties of austenitic stainless steel were investigated in this study. The samples were prepared in accordance to standard samples preparation for wear and hardness test. Pack boronizing were conducted using EKabor®1 powder medium at two different temperatures which are 850°C and 950°C. The wear resistance properties were evaluated though pin on disk test and the surface characterization was analyzed through scanning electron microscopy (SEM), observation. Vickers microhardness tester was performed to obtain the hardness of the samples. The results indicated that there are presences of FeB and Fe2B phases on both samples, but thicker FeB phase was produced at Po-950 samples. This resulted in reduction of abrasion wear properties but major improvement of the hardness properties of boronized stainless steel. © Published under licence by IOP Publishing Ltd.