Investigation of failure analysis on fatigue crack initiation influenced by critical resolved shear stress in X10CrMoVNb9-1 steel
This study investigates the influences of the critical resolved shear stress (CRSS) values on calculating the number of cycles for the fatigue crack initiation cycle of X10CrMoVNb9-1 (P91) under cyclic loading conditions at room temperature while considering varied surface roughness on microstructur...